本公司长期现货供应美国陶氏的PC料,型号: 8600-10, 可为您开增值税票，提供原料SGS认证 ROHS报告 FDA认证等， 欢迎您来电洽谈！ | 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | | 物理性能 | 比重 | | ASTM D792,ISO 1183/B | 1.20 | g/cm3 | | | 熔体流动速率 | 300℃/1.2kg | ASTM D1238,ISO 1133 | 10 | g/10min | | | 成型收缩率 | 流动 | ASTM D955 | 0.50-0.70 | % | | | | 流量 | ISO 294-4 | 0.50-0.70 | % | | 硬度 | 洛氏硬度 | R计秤,3.18mm | ASTM D785 | 123 | | | | | R计秤,4.00mm | ISO 2039-2 | 123 | | | 机械性能 | 拉伸模量 | 3.18mm | ASTM D638 | 2210 | MPa | | | | 4.00mm | ISO 527-2/50 | 2200 | MPa | | | 拉伸强度 | 屈服,3.18mm | ASTM D638 | 60.0 | MPa | | | | 屈服,4.00mm | ISO 527-2/50 | 60.0 | MPa | | | | 断裂,3.18mm | ASTM D638 | 57.9 | MPa | | | | 断裂,4.00mm | ISO 527-2/50 | 58.0 | MPa | | | 伸长率 | 屈服,3.18mm | ASTM D638 | 6.2 | % | | | | 屈服,4.00mm | ISO 527-2/50 | 6.0 | % | | | | 断裂,3.18mm | ASTM D638 | 110 | % | | | | 断裂,4.00mm | ISO 527-2/50 | 110 | % | | | 弯曲模量 | 3.18mm | ASTM D790 | 2400 | MPa | | | | 4.00mm | ISO 178 | 2400 | MPa | | | 弯曲强度 | 3.18mm | ASTM D790 | 93.8 | MPa | | | | 4.00mm | ISO 178 | 94.0 | MPa | | | 悬壁梁缺口冲击强度 | 23℃,3.18mm | ASTM D256 | 747 | J/m | | | | 23℃ | ISO 180/A | 10.0 | kJ/m2 | | | 装有测量仪表的落镖冲击 | 23℃,3.18mm | ASTM D3763 | 58.8 | J | | 热性能 | 热变形温度 | 0.45MPa,未退火 | ASTM D648,ISO 75-2/B | 139 | ℃ | | | | 1.8MPa,未退火 | ASTM D648 | 127 | ℃ | | | | 1.8MPa,未退火 | ISO 75-2/A | 125 | ℃ | | | 维卡软化温度 | | ASTM D1525 | 149 | ℃ | | | | | ISO 306/A120 | 150 | ℃ | | | | | ISO 306/B50 | 144 | ℃ | | | 球压温度 | | IEC 60335-1 | >125 | ℃ | | | 线形膨胀系数 | 流动(-22到85℃) | ASTM D696 | 0.000065 | cm/cm/℃ | | 可燃性 | UL阻燃等级 | 1.59mm | Internal Method | V-0 | | | | 热灯丝点火温度 | 2.00mm | IEC 60695-2-13 | 960 | ℃ | | | 极限氧指数 | | ASTM D2863,ISO 4589-2 | 35 | % | | UL746 | RTI Str | | UL 746 | 125 | ℃ | | | RTI lmp | | UL 746 | 125 | ℃ | | | RTI Elec | | UL 746 | 125 | ℃ |
| | | |
| | |
|